Class: ER317L
AWS: A5.9
Conforms to Certification: AWS A5.9 ASME SFA A5.9
Weld Process Used for Mig (GMAW) and Submerged Arc (SAW)
AWS Chemical Composition Requirements
C = 0.03 max
Cr = 18.5 – 20.5
Ni = 13.0 – 15.0
Mo = 3.0 – 4.0
Mn = 1.0 – 2.5
Si = 0.30 – 0.65
P = 0.03 max
S = 0.03 max
Cu = 0.75 max
| Available Sizes | |
| Diameter X Spool Sizes | Diameter X Coil Sizes |
| .025 x 2#, 10#, 25# | 1/16 x 60# & mill coil |
| .030 x 2#, 10#, 25#, 30#, 33# | 5/64 x 60# & mill coil |
| .035 x 2#, 10#, 25#, 30#, 33# | 3/32 x 60# & mill coil |
| .045 x 2#, 10#, 25#, 30#, 33# | 1/8 x 60# & mill coil |
| 1/16 x 10#, 25#, 30#, 33# | 3/16 x 60# & mill coil |
| 5/32 x 60# & mill coil | |
Application
ER317L is used for welding stainless steels with similar composition. Due to its higher molybdenum content, this alloy offers high resistance to pitting and crevice corrosion. Lower carbon makes the weld metal less susceptible to inter-granular corrosion.
| Deposited Chemical Composition % (Typical) | ||
| C = 0.02 | Mo = 3.40 | P = 0.010 |
| Cr = 18.50 | Mn = 1.70 | S = 0.012 |
| Ni = 13.20 | Si = 0.40 | |
| Mechanical Properties (R.T.) | |
| Yield Strength | 55,000psi |
| Tensile Strength | 87,000psi |
| Elongation | 47% |
| Reduction of Area | 70% |
Deposited All Weld Metal Properties
Data is typical for ER317L weld metal deposited by Mig using Argon + 2% oxygen as the shielding gas. Data on sub-arc is not presented, as sub-arc is dependent on the type of flux used.
| Recommended Welding Parameters | ||||||
| GMAW “Mig Process” | Reversed Polarity | |||||
| Wire Diameter | Wire Feed | Amps | Volts | Shielding Gas | Gas CFH | |
| Short Arc Welding | .030 | 13-26 | 40-120 | 16-20 | Argon+2% O2 | 25 |
| .035 | 13-26 | 60-140 | 16-22 | Argon+2% O2 | 25 | |
| Spray Arc Welding | .035 | 20-39 | 140-220 | 24-29 | Argon+2% O2 | 38 |
| .045 | 16-30 | 160-260 | 25-30 | Argon+2% O2 | 38 | |
| 1/16 | 10-16 | 230-350 | 27-31 | Argon+2% O2 | 38 | |
Other shielding Gases may be used for Mig welding. Shielding gases are chosen taking Quality, Cost, and Operability into consideration
| Recommended Welding Parameters | ||
| SAW “Submerged Arc Welding Process” | REversed Polarity Suggested | |
| Wire Diameter | Amps | Volts |
| 3/32 | 250-450 | 28-32 |
| 1/8 | 300-500 | 29-34 |
| 5/32 | 400-600 | 30-35 |
| 3/16 | 500-700 | 30-35 |
Both Agglomerated and fused fluxes can be used for submerged arc welding.
Note: The chemical composition of the flux mainly affects the chemistry of the weld metal and consequently its corrosion resistance and Mechanical properties.